The Material Witness: Nonwoven Aramid Reinforcement is Back


Reading time ( words)

In the 1st century AD, there was significant debate among Jewish theologians as to whether resurrection was possible. PCB designers in the early 21st century have had a similar concern about future availability of 85NT nonwoven aramid laminate and prepreg. The stakes may be somewhat less critical, depending on your theological bent, but the future of a wide variety of programs designed around the properties of (dare I mention the name?) Thermount® have been hanging in the balance. What was Thermount exactly and why was there such a furor when DuPont announced its premature demise?  And where do we stand now with the redevelopment of a nonwoven aramid product?

The original 85NT product was based on high tensile-strength para-aramid fiber with a meta-aramid fibrid binder. The para-aramid fibers have a high tensile modulus (fiber modulus of about 19 mpsi) and a negative linear coefficient of thermal expansion with a CTE of about -4 ppm/oC meaning that the material shrank when heated, and the fibrid held the fibers together in a uniform matrix. Produced in a high-end papermaking process, the resulting substrate was a yellow aramid paper material that produced laminates with a unique and useful set of properties. For a polyimide aramid composite the benefits look like this: 

  • Tg of pure polyimide (250oC)
  • Low in-plane (X,Y) expansion of 7-9 ppm/°C
  • Excellent dimensional stability and enhanced registration
  • Decomposition temperature of 426°C, compared with 300-360°C for typical high-performance epoxies, offering outstanding high-temperature life
  • Polymeric reinforcement results in PCBs typically 25% lighter in weight than conventional glass-reinforced laminates
  • Laser ablatable for high-speed formation of microvias as small as 25μm in clad laminates as thin as 0.002”
  • Electrical and mechanical properties meeting the requirements of IPC-4101/53
  • Compatible with lead-free processing
  • RoHS/WEEE compliant

Chet Oct 2015 Fig 1.JPGThe earliest military adoption of aramid reinforced laminates was in the guidance system for the Tomahawk cruise missile, a significant success in terms of test results (thermal cycled better than the prior woven aramid technology) and field performance. The combat-proven Tomahawk gave the then relatively new substrate a kick-start. I still have the jacket patch that the Tomahawk PWB development staff gave me.  And there was some real pride in achievement in the ongoing field success of that program.

Later uses of 85NT materials included a wide variety of military and commercial avionics. The first-generation avionics for the Boeing 777 were designed on this platform, and it replaced heavy copper-invar-copper (CIC) in a number of older designs. In addition to these, the Iridium telecommunications satellite constellation used 85NT for a number of its PWBs.

In July of 2006 the imminent demise of the DuPont Thermount product was announced to its customer base. In November 2006, a letter from Ralph Hutton, president of DuPont Teijin Advanced Papers, said, “Due to a dramatic reduction in demand for Thermount reinforcement for consumer applications in Japan, and a corresponding reduction in global demand for the foreseeable future, we are unable to continue accepting orders for Thermount reinforcement of any kind beyond December 31, 2006.” 

Working with senior officials at major military and commercial OEMs, Arlon procured and stocked sufficient NWA product to sustain existing programs during the period required to find a suitable alternative source.

Well, nonwoven aramid is back. Although I have tried to keep this column non-commercial, Arlon is, as best I know, the only company that has committed the resources and time to work with potential suppliers to develop a polyimide NWA that meets all the performance criteria of the original 85NT product. 

In fact, what we have now is a drop-in replacement that will match both in process and properties of the original. That was not easy to accomplish and several very well qualified vendors tried and failed to meet the exacting requirements for the substrate. The project took longer than had originally been expected, though stocks of the old material have held up well enough to protect ongoing programs for the entire duration of the development program. 

Chet Oct 2015 table 1.JPG

As you can see from the following microphotographs, the registration and hole quality of the new aramid reinforcement is essentially identical to that of the original DuPont product. The12-layer test coupons were made in the same press and lamination cycle using parameters developed for the original 85NT product. 

For those who have been frustrated trying to find alternative technologies for their critical SMT boards, I think I can say with a great degree of confidence that Arlon’s 85NT is back and that you won’t be disappointed with its processability or performance. 

Chet Oct 2015 Fig 2.JPG

Until next time, this is the Material Witness wishing you happy fabrication and a great fall 2015. 

Chet Guiles is a consultant for Arlon Electronic Materials.

 

 

 

Share


Suggested Items

Judy Warner: AltiumLive’s Second Year to be Even Better Than First

09/19/2018 | Andy Shaughnessy, Design007
Last year, Altium launched its AltiumLive event with shows in San Diego and Munich, Germany. This year, the event has expanded to include an extra day of classes. Altium is gearing up for the San Diego event in early October and the German show in January 2019. I recent spoke with Judy Warner, director of community engagement for Altium, about what designers should expect at both shows, and how the company can build on the success of the 2017 events going into the future.

BGA Fanout Routing Overview

09/04/2018 | Christian Keller, Altium
PCB developers are deluged with new challenges caused by increasing density and smaller components. Ball grid arrays (BGAs) create particular challenges during layout, with hundreds of connections in just a few square centimeters. Fortunately, designers now have options for addressing these issues.

Excerpt: The Printed Circuit Designer’s Guide to…Flex and Rigid-Flex Fundamentals

06/25/2018 | Dave Lackey and Anaya Vardya, American Standard Circuits
The design process is arguably the most important part of the flex circuit procurement process. The decisions made in the design process will have a lasting impact, for better or worse, throughout the manufacturing cycle. In advance of providing important details about the actual construction of the flex circuit, it is of value to provide some sort of understanding of the expected use environment for the finished product.



Copyright © 2018 I-Connect007. All rights reserved.